Product Details:
|
| Technique: | ESR Hot Rolled, Forged, EAF+LF+VD+Hot Rolled/Forged, Forged/Hot Rolled/Cold Drawn, Hot Rolled/forged/cold Draw | Surface Treatment: | Black Or Machined, Black Bright Mirror(mill Polishing HL Etc), Black Surface Or Mi |
|---|---|---|---|
| Length: | Customized, Customers' Requirement, 3000-118800mm, As Buyer Requirement | Application: | Plastic Mold |
| Standard: | AISI, DIN, ASTM, GB, JIS | Grade: | S136/1.2083/420/SUS420J2/4CR13/40CR14 |
| Type: | Steel Plate | Material: | Plastic Tool Steel, EAF Or ESR, Alloy Tool Steel |
| Surface: | Black Or Polish, Black Surface/machined Surface/bright Surface, Polished, Machined | Shape: | Plate, Sheet, Steel Plate/flat Bar/round Bar, Plate/sheet/ Flat Bar, Bar |
| Hardness: | 30-35 HRC 35-45 HRC | Packing: | Raw, According To The Demand Of The Customer Inquire, Standard Seaworthy Package |
| Highlight: | S136 Plastic Mold Steel Plate,1.2083 Plastic Mold Steel,4Cr13 Plastic Mold Steel |
||
Takford special steel is one of the professional suppliers of 1.2083 Mold Steel, We supply 1.2083 Steel Round bar, Flat bar, Plates. S136 tool Steel China supplier and stockholders.We are the biggest the stockholders for 1.2083 in China. Thickness from 8mm up to 500mm, wide max do 2200mm
DIN 1.2083 Mold Steel material by electroslag melting smelting with good cast optical activity (mirror processing) good wear resistance and toughness at high temperature with good plasticity because of its high chromium content (13.6%) so its corrosion resistance is excellent, pre-add hard corrosion-resistant mirror mold steel S136 is a mirror rust-proof mold steel.
S136 mold steel with excellent corrosion resistance has been widely applied in the mold industry. However, in order to meet the increasing demands of injection products with complex structure and high quality, selective laser melting (SLM) as a novel manufacturing method is chosen due to its rapid fabricating parts with complex geometric shapes. Further, it is essential to enhance their hardness and wear property to prolong the service life of the injection mold.
| C | Si | Mn | Cr | P | S |
| 0.38 | 0.8 | 0.5 | 13.6 | <0.03 | <0.03 |
| Grade: | S136 / AISI 420 / DIN 1.2083 / GB 4Cr13 | Hardness: | ≤ 229HBS Or 32~36HRC |
| Hot Rolled Technology: | EAF+LF+VD | Hardness(HRC): | 49 47 46 46 47 32 |
| Applications: | High Quality Plastic Mould, Transport Plastic Mould | ||
Equivalent grades: 4CR13/HPM38/S-STAR/PAK90/2083/420/M300 Die Steel
Heat treatment
1.Annealing
In a protected state, heat up to 780 ℃ and then cool to 650 ℃ in the furnace at 10 ℃ per hour and then cool in the air.
2.Stress elimination
After roughing, must be heated to 650 ℃, both hot 2 hours, slowly cooling to 500 ℃, and then cooling in the air.
3.Hardened
Preheating Temperature: 600-850 ℃
Quenching temperature: 980-1050 ℃
High degree of polishing and high requirements of the internal mold, corrosion-resistant plastic molds, production, medical, food industry, and other products. S136 can be used with all molds, due to their special nature, more suited to the needs of special environments.