|Technique:||Hot Rolled, Forged, EAF+LF+VD+Hot Rolled/Forged, Forged/Hot Rolled/Cold Drawn, Hot Rolled/forged/cold Draw||Surface Treatment:||Black Or Machined, Black Bright Mirror(mill Polishing HL Etc), Black Surface Or Mi|
|Length:||Customized, Customers' Requirement, 3000-118800mm, As Buyer Requirement||Application:||Plastic Mold|
|Standard:||AISI, DIN, ASTM, GB, JIS||Grade:||S136/1.2083/420/SUS420J2/4CR13/40CR14|
|Type:||Rounf Bar||Material:||Plastic Tool Steel, EAF Or ESR, Alloy Tool Steel|
|Surface:||Black Or Polish, Black Surface/machined Surface/bright Surface, Polished, Machined||Shape:||Plate, Sheet, Steel Plate/flat Bar/round Bar, Plate/sheet/ Flat Bar, Bar|
|Hardness:||Annealing Below 230HB||Delivery Condition:||Hot Forged +Rough Machined (black Surface, N+T, T, Without Packed, OT|
|Heat Treatment:||Pre-harden HRC28-36, Annealed; Q+T||Packing:||Raw, According To The Demand Of The Customer Inquire, Standard Seaworthy Package|
4CR13H 1.2083 Steel round bar,
dia6mm 1.2083 Steel round bar,
4CR13H hot rolled round bar
Takford special steel is one of the professional suppliers of S136 Mold Steel, We supply S136 Steel Round bar, Flat bar, Plates. S136 tool Steel China supplier and stockholders.We are the biggest the stockholders for S136 in China. Thickness from 8mm up to 500mm, wide max do 2200mm
4CR13 Mold Steel material by electroslag melting smelting with good cast optical activity (mirror processing) good wear resistance and toughness at high temperature with good plasticity because of its high chromium content (13.6%) so its corrosion resistance is excellent, pre-add hard corrosion-resistant mirror mold steel S136 is a mirror rust-proof mold steel.
S136 mold steel with excellent corrosion resistance has been widely applied in the mold industry. However, in order to meet the increasing demands of injection products with complex structure and high quality, selective laser melting (SLM) as a novel manufacturing method is chosen due to its rapid fabricating parts with complex geometric shapes. Further, it is essential to enhance their hardness and wear property to prolong the service life of the injection mold.
|Grade:||S136 / AISI 420 / DIN 1.2083 / GB 4Cr13||Hardness:||≤ 229HBS Or 32~36HRC|
|Hot Rolled Technology:||EAF+LF+VD||Hardness(HRC):||49 47 46 46 47 32|
|Applications:||High Quality Plastic Mould, Transport Plastic Mould|
Equivalent grades: 4CR13/HPM38/S-STAR/PAK90/2083/420/M300 Die Steel
In a protected state, heat up to 780 ℃ and then cool to 650 ℃ in the furnace at 10 ℃ per hour and then cool in the air.
2. Stress elimination
After roughing, must be heated to 650 ℃, both hot 2 hours, slowly cooling to 500 ℃, and then cooling in the air.
Preheating Temperature: 600-850 ℃
Quenching temperature: 980-1050 ℃
High degree of polishing and high requirements of the internal mold, corrosion-resistant plastic molds, production, medical, food industry, and other products. S136 can be used with all molds, due to their special nature, more suited to the needs of special environments.
Contact Person: Merain Pan
Technique: Hot Rolled, Forged, EAF+LF+VD+Hot Rolled/Forged, Forged/Hot Rolled/Cold Drawn, Hot rolled/forged/cold draw
Surface treatment: black or machined, Black Bright Mirror(mill Polishing HL Etc), black surface or mi
Length: Customized, Customers' Requirement, 3000-118800mm, As Buyer requirement
Application: mould steel, Boiler Plate, Flange Plate,tool steel