C45 Carbon Steel Plate tool steel plate for mold base

Certification
China DONGGUAN MISUNG MOULD STEEL CO.,LTD certification
Customer Reviews
We are almost finish with the assembly of the Tool, the dimensions and workmanship is very good, we are impressed by your standards. We have to do some testing of tool to give complete feedback but so far we happy with your quality, thank you and have a nice day.

—— Will Smith

I am very happy with your products, you are the best suppliers for us.

—— JAHANZAIB

We work with takford for more than 6 years, takford is the trusted suppliers.

—— Shahin shahi Pasand

I'm Online Chat Now

C45 Carbon Steel Plate tool steel plate for mold base

C45 Carbon Steel Plate tool steel plate for mold base
C45 Carbon Steel Plate tool steel plate for mold base C45 Carbon Steel Plate tool steel plate for mold base C45 Carbon Steel Plate tool steel plate for mold base C45 Carbon Steel Plate tool steel plate for mold base C45 Carbon Steel Plate tool steel plate for mold base C45 Carbon Steel Plate tool steel plate for mold base

Large Image :  C45 Carbon Steel Plate tool steel plate for mold base

Product Details:
Place of Origin: CHINA
Brand Name: misung steel
Model Number: C45/1045/S45C
Payment & Shipping Terms:
Minimum Order Quantity: 1 PIECE
Price: 0.5-2USD/KG
Packaging Details: Standrad export seaworthy package/ wooden box package
Delivery Time: 5-10 DAYS
Payment Terms: L/C, T/T, Western Union
Supply Ability: 1000 TONS PER MONTH

C45 Carbon Steel Plate tool steel plate for mold base

Description
Application: Mold Base, Mold Steel, Tool Standard: JIS,GB,ASTM
Surface Treatment: BLACK Technique: HOT ROLLED
Grade: C45/1045/S45C Thickness: FROM 6MM UP TO 800MM
Length: CUSTOM-MADE Type: MOLD INDUSTRY
Product Name: C50/1050/S50C Section Shape: PLATE
Alloy Or Not: ALLOY Standard2: MOLD INDUSTRY
Width: CUSTOM-MADE Material: CARBON STEEL SERIES
High Light:

C45 Hot Rolled Carbon Steel

,

C45 Carbon Steel Plate

,

Hot Rolled Carbon Steel Plate

Hot rolled C45 medium carbon steel plate for standard mold base
 
Description:
The medium carbon high strength carbon structural steel has high strength and hardness after quenching. The steel has medium machinability, low cold deformation plasticity, poor weldability, no temper brittleness during heat treatment, but low hardenability. The critical diameter in water is 13 * 30MM, and there is cracking tendency during water quenching. This steel is usually used after heat treatment such as normalizing, quenching and tempering, or high frequency surface quenching.
50 steel can be hardened to hrc42 ~ 46. Therefore, if the surface hardness is needed and the superior mechanical properties of 50 steel are expected to be exerted, the surface hardness of 50 steel can be obtained by carburizing and quenching.
 

1.Supply Form & Size & Tolerance

Supply Form Size(mm) Process Tolerance



Round
Φ6-Φ100 Cold Drawn Bright/Black Best H11

Φ16-Φ350

Hot Rolled
Black -0/+1mm
Peeled/ground Best H11

Φ90-Φ1000

Hot Forged
Black -0/+5mm
Rough Turned -0/+3mm

Flat/Square/Block
Thickness :120-800
Hot Forged
Black -0/+8mm
Width:120-1500 Rough Machined -0/+3mm

Remark:Tolerance can be customized as per requests

2.Chemical Composition

Standard Grade C Si Mn P S Cr
ASTM A29 1045 0.43-0.50  - 0.60-0.90 ≤0.04 ≤0.05  -

EN 10083-2
C45
0.42-0.50

≤0.04

0.50-0.90

≤0.03

≤0.035

≤0.4
1.1191
JIS G4051 S45C 0.42-0.48 0.15-0.35 0.60-0.90 ≤0.03 ≤0.035  -

3.Physical Property

Density, g/cm3 7.87
Melting point °C 1495
Modulus of Elasticity, psi 29 x 10^6
Coefficient of Thermal Expansion, 68-212˚F, /˚F 6.39 x 10^-6
Thermal Conductivity, Btu/ft hr ˚F 30
Specific Heat, Btu/lb ˚F 0.116
Electrical Resistivity, Microhm-in 6.42

4. Mechanical Property

Section Size mm ≤ 16 17 - 40 41 - 100
Tensile Strength Mpa 700-850 6500-800 630-780
Yield Strength Mpa ≥ 500 ≥430 ≥ 370
Elongation in 50mm % ≥ 14 ≥ 16 ≥ 17
Impact Charpy J ≥ 30 ≥ 30 ≥ 30
Hardness HB 210-245 195-235 185-230

Remark:Water Quench at 820°C -850°Cor oil quench at 830°C-860°C and Tempered Between 540°C – 680°C

5. Forging

AISI 1045 is heated in two steps, first to a temperature of 750 oC - 800 oC for a suitable time, then to a temperature of 1100 oC - 1200 oC for a sufficient time for the steel to be thoroughly heated, the minimum forging temperature is 850°C, so do not go below this temperature.

6. Normalizing

Normalizing is used to refine forged structures that may not cool uniformly after forging and is considered a conditioning treatment prior to the final heat treatment. normalizing of AISI 1045 steel should be done at temperatures between 870°C - 920°C, keeping the steel heated for a suitable time to complete the ferrite to austenite transformation.

7. Annealing

Annealing is considered a suitable treatment for processing. aISI 1045 should be carried out at a nominal temperature of 800°C-850°C, maintaining a suitable time to allow the steel to heat sufficiently and then cooling in the furnace.

8. Quenching

AISI 1045 can be quenched to improve surface hardness and strength. Usually heated to 820oC - 860oC, maintained for a suitable time to allow the steel to be heated uniformly, soaked for 10 - 15 minutes per 25mm section, then quenched in water or oil and tempered immediately after quenching.

9. Tempering

AISI 1045 steel is usually heated to 400oC - 650oC as required, maintained until the temperature is uniform throughout the section, immersed for 1 hour per 25mm section and cooled in still air.

10. Applications

Compared to AISI 1020, AISI 1045 has a lower alloy content, but can be fire or induction hardened to achieve high strength and is widely used in many industries where high strength and wear resistance are required.

Typical applications include axles, bolts, connecting rods, hydraulic clamps, rams, pins, rollers, bolts, shafts, spindles, sleeves, light gears, etc.

 