Product Details:
|
| Technique: | Forged, EAF+LF+VD+Hot Rolled/Forged, Forged/Hot Rolled/Cold Drawn, Hot Rolled/forged/cold Draw | Application: | Aluminium Extrusion Mold |
|---|---|---|---|
| Standard: | AISI, DIN, ASTM, GB, JIS | Type: | Alloy Steel Bar, Carbon Steel Bar, Mold Steel, Tool Steel |
| Ut Test Standard: | SEP1921-84 Class3 C/c To D/d | Surface Treatment: | Black Or Machined, Black Bright Mirror(mill Polishing HL Etc), Black Surface Or Mi |
| High Light: | 1.2714 Forged Steel block,1.2714 Tool Steel block,Forged Tool Steel block |
||
Forged Production 1.2714 Tool Steel Block For Aluminium Extrusion Mould
1.2714 steel Packaging & Delivery
| Packaging Details: | seaworthy packing; 20ft: GW:17.5T; (5.80mX2.13mX2.18m,) 40ft: GW:22T; (11.8mX2.13mX2.18m,) |
| Delivery Detail: | 4~7 days after the order is confirmed |
Hot work steel 1.2714 Specifications
Songshun din 1.2714 steel of good price 1.2714
1.A/N/Q+T provide
2.Sample free
3.Black or Bright
4.D: Max:800mm
1.2714 steel Product Description
| Songshun din 1.2714 steel of good price 1.2714 | |||||||||||||||
| 1.Specifications of din 1.2714 steel of good price 1.2714 | |||||||||||||||
| Round bar | Diameter(mm) | Length (mm) | |||||||||||||
| 20~800 | 3000~5800 | ||||||||||||||
|
Plate |
Thickness(mm) | Width (mm) | Length (mm) | ||||||||||||
| Max:800 | 205~810 | 2000~4000 | |||||||||||||
| The size can be customed | |||||||||||||||
| 2.Chemical composition(%) of din 1.2714 steel of good price 1.2714 | |||||||||||||||
| C | Si | Mn | Cr | Mo | V | Ni | P | S | |||||||
| 0.50- 0.60 | 0.10- 0.40 | 0.65- 0.95 | 1.00- 1.20 | 0.45-0.55 | 0.07-0.12 | 1.50-1.80 | 0.03max | 0.03max | |||||||
| Similar standards | |||||||||||||||
| AISI/SAE | DIN | W.Nr. | JIS | GB,YB | |||||||||||
| 6F2 | 56NiCrMoV7 |
1.2713 1.2714 |
SKD4 | SCrNiMo | |||||||||||
| 3.Heat treatment of din 1.2714 steel of good price 1.2714 | |||||||||||||||
|
Isothermal annealing: -Heat to 800°Cand hold at temperature for 1/2 h to 1 h; -Furnace cooling to 670°Cand hold at temperature for at least 10 hours; -Cool by 10°C/h to 630°C; -Cooling in air. Maximum hardness:≤240 HB |
|||||||||||||||
|
Stress relieving: To be carried out after maching before the final heat treatment. -Heat to 600-650°C, hold for 4-6 hours; -Cooling in furnace to 300-350°C; -Cooling in air |
|||||||||||||||
|
Hardening: -Initial preheating to 350-450°C; -Second preheating to 650-750°C; -Heat to hardening temperature 860-890°Cand hold at temperature; -Cooling in hot oil (40-60°C); Tempering hardness: 45~45HRC |
|||||||||||||||
|
Tempering: Tempering must be carried out within one hour from hardening(warm part) in the range 550-630°Cfor 4-6 hours according to hardness required, the dimensions of the parts and operating conditions. |
|||||||||||||||